Method Development in Thermal Analysis: Part 2

Step 4: Choosing the Temperature Program 

The two main aspects that have to be considered are the

  • Type of temperature program (single segment, multi-segment, modulated temperature program).
  • Choice of parameters (heating rate, start and end temperatures, and if relevant, amplitude and period).

Choice of parameters (heating rate, start and end temperatures, and if relevant, amplitude and period).

  • Thermal conductivity of the sample: the temperature distribution in the sample should always be as homogeneous as possible (" low heating rates).
  • The lower the heating rate, the better the temperature resolution
  • The higher the heating rate, the more pronounced the effects (DSC, SDTA).
  • Start and end temperatures: the time interval before and after the first and last thermal events should be sufficiently long to enable a clear “baseline” to be drawn. Recommended values: DSC 3 min, TGA: 5 min, TMA: 5 min, DMA 8 min. 

In standard methods, for example ASTM and DIN, the temperature program is often specified. According to ISO 17025, such standard methods no longer need to be validated. This should, however, be treated with caution because many standard methods are not fully validated.

In practice, variations of standard methods are often used that most certainly require validation. 

 

 

Step 5: Choosing the Atmosphere  

With DSC and TGA in particular, different atmospheric conditions allow different types of information to be obtained. This is illustrated in Figure 1, which describes the decomposition of coal as an example. The upper curve was measured in an air atmosphere, the lower curve under nitrogen (up to 900 °C) and then air (above 900 °C). In air, the combustion profile of the sample is of interest, that is, the temperature at which the coal begins to burn, and how the combustion process proceeds. If the measurement is first performed in an inert atmosphere and then finally under air, the main questions have to do with the composition of the coal, that is, the content of volatile compounds (moisture, adsorbed gases), whether inorganic compounds are present, and the carbon content.

In DSC, the atmosphere within the crucible plays an important role. For example, in an open crucible, one observes the slow evaporation of solvents and moisture. This process gives rise to broad endothermic peaks that sometimes overlap with other interesting effects such as glass transitions and polymorphic transitions.

If the crucible is sealed with a crucible lid that has been pierced with a small hole, a so-called self-generated atmosphere is created and the evaporation process is delayed almost to the boiling point of the liquid. Above the boiling point, the liquid evaporates rapidly from the crucible. METTLER TOLEDO supplies lids with a hole-diameter of 50 µm for this type of measurement. Finally, in a hermetically sealed crucible, the boiling point can be exceeded. The crucible is then under pressure. This can lead to initial deformation of the crucible and ultimately, on further temperature increase, to bursting (see Figure 2). Endothermic evaporation can be completely suppressed by using medium pressure crucibles. 

 

Step 6: Examining the Sample after Measurement

One should make a habit of weighing samples before and after an experiment (even with TMA and DMA measurements). Small mass changes indicate that evaporation or initial decomposition processes have taken place. This usually has an effect on the measurement curves (not only DSC, but also TMA and DMA curves). These effects are often only weak and may hardly be noticeable so that the gravimetric information is very important. 

Method development in thermal analysis. Part 2: | Thermal Analysis Application No. UC 221 | Application published in METTLER TOLEDO Thermal Analysis UserCom 22