Thermal Analysis Crucibles

There are several factors to consider when selecting a thermal analysis crucible. One must take all factors into account to ensure that the crucibles selected will provide the best results for any DSC, TGA or TGA/DSC measurement. Factors to consider: crucible material, crucible volume, crucible mass, sample under examination, sample robot, experimental conditions (temperature range of measurement, atmosphere, thermal analysis technique used)

• Alumina (aluminum oxide) crucibles– These are the most common crucibles for TGA measurements. They are inert and can handle temperatures up to 1600 °C. Alumina crucibles are used for TGA/DSC as well, but the heat flow signal (SDTA) will be suppressed. It is not recommended to use this type of crucible for DSC measurements. These crucibles can be easily cleaned and reused.
  
• Aluminum crucibles – These are the standard crucibles used for DSC measurements. The thermal conductivity of aluminum is particularly good, therefore thermal effects are easily seen. Aluminum crucibles come in many sizes, can be hermetically sealed, and can be used close to the melting point of aluminum (< 660 °C).
  
• Gold crucibles – A noble metal and therefore these crucibles are chemically resistant. They will avoid any possible reactions with a sample. The thermal conductivity of gold is high, allowing thermal events to be easily seen. The drawback to using gold crucibles is their high price.
  
• Copper crucibles – Used almost exclusively for the determination of oxidative stability or oxidation induction time (OIT) experiments. Copper acts as a catalyst to speed up the oxidation.
  
• Platinum crucibles – Mainly used for TGA/DSC or DSC measurements at temperatures above 640 °C. SDTA and DSC curves measured with platinum crucibles are usually better than those obtained using crucibles made of alumina, which has a lower thermal conductivity. However, it should be noted that molten metals form alloys with platinum very easily.
  
• Stainless Steel crucibles – These crucibles are used when high-pressure is needed. They have a threaded opening system so the crucibles can be reused. They are heavier than other metal crucibles, which leads to lower temperature gradients if needed, stainless steel crucibles can be coated with gold to avoid any unwanted reactions with a sample.
  
• Glass crucibles – Used when visual observation of the sample is needed. They are commonly used together with hot-stage microscopy or other thermo-optical analysis methods.
  
• PCA/Sapphire crucibles – PCA is a polycrystalline alumina oxide with properties similar to sapphire. Thanks to its material structure, PCA is very tight, chemically resistant, and inert. The PCA crucible can be recommended for all materials, including melting metals such as Fe or Ni.